Part #
|
L1
|
L2
|
h
|
Type
|
Materials
|
Rect 50*50*3
|
50
|
50
|
3
|
F
|
SSiC
AL2O3 99% AL2O3 99.5% |
Rect 50*50*4
|
50
|
50
|
4
|
F
|
|
Rect 50*50*5
|
50
|
50
|
5
|
F
|
|
Rect 50*50*7
|
50
|
50
|
7
|
F
|
|
Rect 50*50*8
|
50
|
50
|
8
|
F
|
|
Rect 50*50*10
|
50
|
50
|
10
|
F
|
|
Rect 50*50*10.2
|
50
|
50
|
10.2
|
F
|
|
Rect 50*50*10.3
|
50
|
50
|
10.3
|
F
|
|
Rect 50*50*11
|
50
|
50
|
11
|
F
|
|
Rect 50*50*12
|
50
|
50
|
11
|
F
|
|
Rect 50*50*13
|
50
|
50
|
11
|
F
|
|
Rect 100*100*8
|
100
|
100
|
8
|
F
|
|
Rect 35*35*6
|
35
|
35
|
6
|
F
|
|
Rect 35*35*8
|
35
|
35
|
8
|
F
|
|
Rect 3*4*36
|
3
|
4
|
36
|
F
|
|
Rect 20*5*35
|
20
|
5
|
35
|
F
|
|
Rect 10*10*10
|
10
|
10
|
10
|
F
|
|
Curved Rect 50*50*3.3
|
50
|
50
|
3.3
|
A
|
|
Curved Rect 50*50*6
|
50
|
50
|
6
|
A
|
|
Curved Rect 50*50*7
|
50
|
50
|
7
|
A
|
|
Curved Rect 50*50*7.5
|
50
|
50
|
7.5
|
A
|
|
Curved Rect 50*50*8
|
50
|
50
|
8
|
A
|
|
Curved Rect 50*50*8.5
|
50
|
50
|
8.5
|
A
|
|
Curved Rect 50*50*9
|
50
|
50
|
9
|
A
|
|
Curved Rect 50*50*9.1
|
50
|
50
|
9.1
|
A
|
|
Curved Rect 50*50*10
|
50
|
50
|
10
|
A
|
|
Curved Rect 25*50*3.3
|
25
|
50
|
3.3
|
B
|
|
Curved Rect 25*50*5
|
25
|
50
|
5
|
B
|
|
Curved Rect 25*50*8
|
25
|
50
|
8
|
B
|
|
Curved Rect 25*50*9
|
25
|
50
|
9
|
B
|
|
Curved Rect 25*50*10
|
25
|
50
|
10
|
B
|
|
Curved Rect 25*50*12
|
25
|
50
|
12
|
B
|
|
Curved Rect 40*50*10
|
40
|
50
|
10
|
B
|
|
Curved Rect 50*25*6
|
50
|
25
|
6
|
C
|
|
Curved Rect 50*25*7
|
50
|
25
|
7
|
C
|
|
Curved Rect 50*25*9
|
50
|
25
|
9
|
C
|
|
Curved Rect 50*25*10
|
50
|
25
|
10
|
C
|
Sintered Silicon Carbide (SSiC) Physical Property |
||
Technical Parameter | Unit | SSiC |
Hardness | HS | 115 |
Porosity Rate | % | <0.2 |
Density | g/cm3 | >3.10 |
Compressive Strength | MPa | >2500 |
Fractural Strength | MPa | >380 |
Coefficient of Heat Expansion | 10-6/°C | 4.2 |
Content of Sic | % | ≥98 |
Free Si | % | ≤1 |
Elastic Modulus | GPa | ≥410 |
Fracture Toughness | Mpa/m2 | ≥3.42 |
Temperature | °C | 1400 |
AL2O3 Ceramic Physical Property | |||
Technical Parameter | Unit | AL2O3 99% | AL2O3 99.5% |
Content of Al2O3 | % | 99 | 99.5 |
Density | g/cm3 | 3.88 | 3.9 |
Hardness | HRA | 88 | 90 |
Porosity Rate | % | <0.2 | <0.15 |
Fractural Strength | Mpa | 310 | 350 |
Coefficient of Heat Expansion | 10-6/K | 5.3 | 5.2 |
Modulus of Elasticity | GPa | 300 | 340 |
Thermal Conductivity | W/M.K | 26.7 | 26 |
Download the 2013 Armor Ceramic Tiles Catalogue.
If you have any questions please contact us at: E-Mail about your composite armor systems.